- GRADE: 0220AA
- Density:0.920 g/cm³
- Melt Flow Rate:2.2 g/10min
- PACKAGING: 25 kg Bags
- PRODUCER: AMIRKABIR, SHAZAND
LLDPE 0220AA
Description
LLDPE 0220AA is a linear low-density polyethylene (LLDPE) copolymer, specifically formulated with butene as the comonomer. It contains antioxidants, making it suitable for various film applications, particularly in the production of blown and cast stretch films. This grade is designed for light to medium-duty applications and allows for higher output compared to standard LLDPE butene copolymers.
- Melt Flow Rate (MFR): 2.2 g/10 min (at 190°C/2.16Kg)
- Density: 0.920 g/cm³
- Impact Strength: 130 g
- Tear Strength: 300 g/25μ (TD), 110 g/25μ (MD)
- Tensile Strength: 28 MPa (TD), 36 MPa (MD)
- Elongation at Break: 800% (TD), 600% (MD)
- Vicat Softening Temperature: 93°C
- Blown Film Production: Ideal for light-duty applications.
- Cast Stretch Film: Offers excellent cling performance and mechanical properties.
- Blending Partner: This can be blended with other LLDPE or LDPE grades to enhance film characteristics.
For optimal processing, it is recommended to maintain a melt temperature of approximately 225 °C during production.
| Property | Value | Unit | Test Method |
| Melt Flow Rate (MFR) | 2.2 | g/10 min | ISO 1133 |
| Density | 0.920 | g/cm³ | ISO 1183 |
| Tensile Strength at Yield MD | 10 | MPa | ISO 527 |
| Tensile Strength at Yield TD | 11 | MPa | ISO 527 |
| Tensile Strength at Break MD | 36 | MPa | ISO 527 |
| Tensile Strength at Break TD | 28 | MPa | ISO 527 |
| Elongation at Break MD | 600 | % | ISO 527 |
| Elongation at Break TD | 800 | % | ISO 527 |
| Tear Strength MD | 110 | g/25μm | ASTM D1922 |
| Tear Strength TD | 300 | g/25μm | ASTM D1922 |
| Dart Drop Impact | 130 | g | ASTM D1709 |
| Vicat Softening Temperature | 93 | °C | ISO 306 |