- GRADE: F232
- Density: 1.04 g/cm3
- MELT FLOW RATE: 14 gr/10 min
- VICAT SOFTENING POINT: 107 °C
- PACKAGING: 25 kg Bags
- PRODUCER: JAM
ABS F232
Description
F232 is a general-purpose, high-flow injection moulding grade of ABS plastic produced by Padjam Polymer Development Company (PJPC) in Iran. It is known for its good impact strength and a density of 1.04.
- General purpose,
- High flow injection moulding Grade
- good impact
- Small and large Household appliances
- Vacuum cleaners
- Toys
- Telephones and consumer electronics
Packaged product should be protected from the atmospheric agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit the following letter
/M indicates increasing values of mattress
| Property | Test Condition | Test Method | Units | Typical Value |
| Density | ISO 1183 | g/cm³ | 1.04 | |
| Water Absorption | ASTM D 570 | % | 0.3 | |
| Melt Flow Rate (MFR) | ISO 1133 | g/10min | 14 | |
| Tensile Strength | 50 mm/min | ASTM D 638 | MPa | 45 |
| Strain at break | 50 mm/min | ASTM D 638 | % | 20 |
| Flexural Strength | 2 mm/min | ASTM D 790 | MPa | 69 |
| Flexural Modulus | 2 mm/min | ASTM D 790 | MPa | 2350 |
| Izod Impact Strength, Notched | +23°C – thickness 3.2 mm | ISO 180/4A | J/m | 170 |
| Izod Impact Strength, Notched | 0°C – thickness 3.2 mm | ISO 180/4A | J/m | 100 |
| Izod Impact Strength, Notched | -20°C – thickness 3.2 mm | ISO 180/4A | J/m | 70 |
| Izod Impact Strength, Notched | -40°C – thickness 3.2 mm | ISO 180/4A | J/m | 50 |
| Izod Impact Strength, Unnotched | +23°C – thickness 4 mm | ISO 180/1A | kJ/m² | 13 |
| Izod Impact Strength, Unnotched | -40°C – thickness 4 mm | ISO 180/1A | kJ/m² | 6 |
| Charpy Impact Strength, Notched | +23°C | DIN 53453 | kJ/m² | 10 |
| Charpy Impact Strength, Unnotched | +23°C | DIN 53453 | kJ/m² | NB |
| Charpy Impact Strength, Unnotched | -40°C | DIN 53453 | kJ/m² | NB |
| Rockwell Hardness | ISO 2039/2 | R109 | ||
| Vicat Softening Temperature | 10 N – 120°C/h | ISO 306/A | ºC | 107 |
| Vicat Softening Temperature | 50 N – 120°C/h | ISO 306/B | ºC | 101 |
| Deflection temperature under load (annealed) | 1.8 MPa – 120°C/h | ASTM D 648 | ºC | 102 |
| Coefficient of linear thermal expansion | ASTM D 696 | 10^-5/ºC | 9 | |
| Thermal Conductivity | ASTM C 177 | W/(Km) | 0.17 | |
| Moulding Shrinkage | ISO 294.4 | % | 0.4-0.6 | |
| Flame behavior | thickness 1.5 mm | UL 94 | class HB | |
| Glow wire test | thickness 3 mm | IEC 60695-2-1 | ºC | 650 |
| Surface resistivity, dry | IEC 60093 | ohm | 10+14 | |
| Volume resistivity, dry | IEC 60093 | ohm*cm | 10+15 | |
| Dielectric strength, dry | IEC 60243 | kV/mm | 30 | |
| Dielectric constant (relative permittivity), 1000 Hz – dry | IEC 60250 | 3.1 | ||
| Dissipation factor, 1000 Hz – dry | IEC 60250 | 15*10^-3 |