- GRADE: E332
- MELT FLOW RATE: 14 gr/10 min
- VICAT SOFTENING POINT: 107 °C
- PRODUCER: JAM
- PACKAGING: 25 kg Bags
ABS E332
Description
This material is characterized by its medium heat resistance, good flow properties, and strong impact strength, making it suitable for various applications, particularly in the automotive industry.
- Good fluidity: Makes it easy to process through injection molding.
- Good impact resistance: Ensures durability of products.
- Excellent thermal stability: Allows for reliable processing without degradation.
- Medium-temperature resistance: Suitable for a range of applications.
- Automative Interior (Trim parts)
- Tiles
| Property | Test Condition | Test Method | Units | Value |
|---|---|---|---|---|
| General | ||||
| Density | ISO 1183 | g/cm³ | 1.04 | |
| Water Absorption | ASTM D 570 | % | 0.3 | |
| Rheological | ||||
| Melt Flow Rate (MFR) | ISO 1133 | g/10min | 10 | |
| Mechanical | ||||
| Tensile Strength | 50 mm/min | ASTM D 638 | MPa | 40 |
| Strain at break | 50 mm/min | ASTM D 638 | % | 75 |
| Flexural Strength | 2 mm/min | ASTM D 790 | MPa | 62 |
| Flexural Modulus | 2 mm/min | ASTM D 790 | MPa | 2200 |
| Izod Impact Strength, Notched | +23°C – thickness 3.2 mm | ISO 180/4A | J/m | 190 |
| 0°C – thickness 3.2 mm | ISO 180/4A | J/m | 115 | |
| -20°C – thickness 3.2 mm | ISO 180/4A | J/m | 90 | |
| -40°C – thickness 3.2 mm | ISO 180/4A | J/m | 85 | |
| +23°C – thickness 4 mm | ISO 180/1A | kJ/m² | 15 | |
| -40°C – thickness 4 mm | ISO 180/1A | kJ/m² | 8 | |
| Charpy Impact Strength, Notched | +23°C | DIN 53453 | kJ/m² | 12 |
| Charpy Impact Strength, Unnotched | +23°C | DIN 53453 | kJ/m² | NB |
| -40°C | DIN 53453 | kJ/m² | NB | |
| Rockwell Hardness | ISO 2039/2 | R111 | ||
| Thermal | ||||
| Vicat Softening Temperature | 10 N – 120°C/h | ISO 306/A | °C | 109 |
| 50 N – 120°C/h | ISO 306/B | °C | 104 | |
| Deflection temperature under load (annealed) | 1.8 MPa – 120°C/h | ASTM D 648 | °C | 103 |
| Coefficient of linear thermal expansion | ASTM D 696 | 10^-5/°C | 9 | |
| Thermal Conductivity | ASTM C 177 | W/(Km) | 0.17 | |
| Moulding Shrinkage | ISO 294.4 | % | 0.4-0.6 | |
| Flammability | ||||
| Flame behavior | thickness 1.5 mm | UL 94 | class HB | |
| Glow wire test | thickness 3 mm | IEC 60695-2-1 | °C | 650 |
| Electrical | ||||
| Surface resistivity, dry | IEC 60093 | ohm | 10+14 | |
| Volume resistivity, dry | IEC 60093 | ohm*cm | 10+15 | |
| Dielectric strength, dry | IEC 60243 | kV/mm | 30 | |
| Dielectric constant (relative permittivity), 1000 Hz, dry | IEC 60250 | 3.1 | ||
| Dissipation factor, 1000 Hz, dry | IEC 60250 | 15*10^-3 |