- GRADE: HD5000S
- DENSITY: 0.954 g/cm³
- Melt Flow Index: 0.8 gr/10min
- PRODUCER: JAM
- Packaging: 25 Kg
Description
The HD5000S is a high-density polyethylene (HDPE) resin, known for its exceptional properties suitable for various applications. It is characterized by its high tensile strength, flexibility, and resistance to impact, making it ideal for manufacturing products such as ropes, fishing nets, agricultural nets, tarpaulins, and woven sacks. These properties are due to their composition and the specific conditions under which they are processed.
- Melt Flow Rate: 0.8 g/10 min at 190°C, indicating its viscosity and how easily it melts and flows during processing.
- Density: 0.954 g/cm³, showing its compactness and weight per unit volume.
- Vicat Softening Point: 125°C, which is the temperature at which the material starts to soften under load.
- Tensile Strength @ Yield: 290 kg/cm², demonstrating its ability to withstand tension before permanent deformation occurs.
- Tensile Strength @ Break: 390 kg/cm², indicating its maximum resistance to being pulled apart.
- Elongation @ Break: >1000%, showing its capacity to stretch significantly before breaking.
- Flexural Modulus: 12000 kg/cm², reflecting its stiffness and resistance to bending.
- Notched Izod Impact Strength: 17 (P)* kg.cm/cm, highlighting its resistance to impact forces.
- Commonly used for monofilament production, agricultural nets, tarpaulins, and woven sacks
| Property | Value | Units | Test Method |
|---|---|---|---|
| Melt Index | 0.8 | g/10min | D1238 |
| Density | 0.954 | g/cm³ | D1505 |
| Vicat Softening Point | 125 | °C | D1525 |
| Flexural Modulus | 1100 | Mpa | D790 |
| Tensile Strength at Yield | 24 | Mpa | D790 |
| Tensile Strength at Break | 39 | Mpa | D638 |
| H.D.T | 75 | °C | D648 |
| Notched Izod Impact @ 23 °C | 400 | J/m | D256/A |