- GRADE: HD6070UA
- DENSITY: 0.960 g/cm³
- MFR: 7 g/10min
- PRODUCER: TABRIZ
- PACKAGING: 25 kg Bags
Description
HDPE HD6070UA is a high-density polyethylene (HDPE) grade known for its narrow molecular weight distribution, making it suitable for a broad range of injection molding applications. This grade of HDPE is characterized by easy processing, good impact strength, and high rigidity, among other properties. It is beneficial for manufacturing crates, boxes, seats, and pallets due to its durability and resistance to deformation.
- Easy Processing: This characteristic makes HDPE 6070 UA versatile for various manufacturing processes, including injection molding.
- High Rigidity: Offers structural integrity and stability, essential for products that need to maintain their shape under load.
- Good Impact Strength: Indicates the material’s ability to absorb energy from an impact, reducing the likelihood of damage during handling or use.
- High Warpage Resistance: This is important for injection-molded parts that need to retain their shape without distortion after cooling.
- UV Stabilization (UA): Incorporates UV protection to prevent degradation from exposure to sunlight, extending the product’s lifespan.
- Crates: HD6070UA is ideal for manufacturing crates due to its durability and resistance to impact.
- Pails and Containers: Its high rigidity makes it suitable for creating pails and containers that can withstand significant pressure and impact.
- Pallets: The material’s strength and stability make it an excellent choice for pallet construction.
- Structural Foam and Seats: HD6070UA’s good impact strength and high rigidity allow it to be used in the production of structural foam components and seating solutions, offering both comfort and durability.
| Property | Unit | Test Method | Typical Value |
|---|---|---|---|
| Melt Flow Index (190°C 2.16KG) | g/10min | ASTM D-1238 | 7 |
| Density | gr/cm3 | ASTM D-1505 | 0.960 |
| Yellow Index | – | ASTM E-313 | -1 |
| Whiteness Index | – | ASTM E-313 | 60 |
| Vicat Softening Point | °C | ASTM D-1525 | 120 |
| Tensile Stress at Yield | MPa | ASTM D-638 | 26 |
| Melting Point | °C | ASTM D-2117 | 132 |
| Elongation at Break | % | ASTM D-638 | 900 |
| Flexural Modulus | MPa | ISO178-197 | 1400 |
| Charpy Impact | KJ/M2 | ASTM D-6110 | 5 |