- GRADE: LFI2047A
- Density: 920 kg/m3
- Melt Flow Rate: 4.7 (190 °C/2.16 Kg)
- PRODUCER: ARYA SASOL
- HS Code: 39011030
- Equivalents: SABIC HP4024WN | SABIC P4024ZN
- PACKAGING: 25 kg Bags
LDPE LFI2047A
Description
LFI 2047A is a low-density polyethylene known for its excellent toughness and optical properties. It includes a moderate amount of antiblock and slip agent (Erucamide) additives, ensuring low energy consumption and good draw-down ability during processing. This grade typically demonstrates low friction and minimal blocking properties, and it is produced using SABTEC licensed technology.
- Good toughness
- Excellent optical clarity
- High processability
- Low energy consumption during production
- Good draw-down ability
LFI2047A is primarily used for blown film extrusion and is suitable for the following applications:
- High clarity laundry bags
- Textile wrapping films
- Zip lock bags
- Surface protection films
- General packaging films
This LDPE grade is produced by ARYASASOL POLYMER Company. It is recommended for blown film extrusion processes, which allow manufacturers to create thin, flexible films with consistent quality.
| Property | Typical Value | Unit | Test Method |
| Melt Flow Index (MFI) (190 °C/2.16 Kg) | 4.7 | dg/min | ISO 1133 |
| Density | 920 | kg/m³ | ISO 1183 |
| Impact Strength | 15 | kJ/m | ASTM D4272 |
| Tear Strength (TD) | 25 | kN/m | ISO 6383-2 |
| Tear Strength (MD) | 80 | kN/m | ISO 6383-2 |
| Yield Stress (TD) | 11 | MPa | ISO 527-1,3 |
| Yield Stress (MD) | 12 | MPa | ISO 527-1,3 |
| Tensile Stress at Break (TD) | 15 | MPa | ISO 527-1,3 |
| Tensile Stress at Break (MD) | 27 | MPa | ISO 527-1,3 |
| Strain at Break (TD) | >500 | % | ISO 527-1,3 |
| Strain at Break (MD) | >100 | % | ISO 527-1,3 |
| Modulus of Elasticity (TD) | 200 | MPa | ISO 527-1,3 |
| Modulus of Elasticity (MD) | 200 | MPa | ISO 527-1,3 |
| Coefficient of Friction | 0.2 | – | ASTM D1894 |
| Blocking | 10 | – | ASTM D3354 |
| Re-blocking | 20 | – | SABTEC method |
| Haze | 9 | % | ASTM D1003 A |
| Gloss (45°) | 55 | GU | ASTM D2457 |
| Clarity | 21 | mV | SABTEC method |
Recommended Process Conditions:
- Extruder temperature profile: 145-160 °C
- Blow up ratio: 2-3
- Film thickness: 25-50 µm