- GRADE: 7000F
- DENSITY: 0.950-0.954 g/cm³
- Melt Flow Rate (MFR): 0.03-0.05 gr/10min
- Equivalents: SABIC® HDPE F00950 – SABIC® HDPE F00952
- Packaging: 55*25 Kg shrink-wrapped wooden pallets
- Recommended Film Thickness: 10-25 microns.
- PRODUCER: BAKHTAR, ILAM, MEHR
HDPE 7000F
Description
HDPE 7000F is a high-density polyethylene copolymer for thin films with high strength and stiffness. Its unique molecular structure and density make it easy to extrude and has high melt strength. It is perfect for applications that require durable and reliable thin films.
- High Mw & Broad Mw Distribution: Easy to extrude and high melt strength.
- High Tensile: Durable and tear resistant.
- Good Dart Impact: Impacts don’t break the pack.
- Low Gel: Smoother and clearer films for better looks and functionality.
- Good Moisture Barrier: Protects contents from moisture damage and keeps them fresh.
- Ultra Thin Film Production: Can produce thinner and lighter films without sacrificing strength.
- Food Contact: Safe for direct food contact, opens up more food industry applications.
- High Stiffness: Retains shape and resists deformation under stress for bags and other packaging.
- Wide Service Temperature Range: Performs well in various temperatures for multiple applications.
- UV Resistance: Protects from UV rays and extends product life, especially for outdoor use.
- Good Impact: Impacts and rough handling won’t break the pack.
- Good Processability: Easy to process and mold for efficient production.
- Contains Antioxidants and Acid Scavengers: These additives enhance the material’s stability and longevity.
HDPE 7000F is suitable for various uses, especially in the packaging industry, due to its robust properties and thin film production:
- Films: 10-25 microns
- Public Use Films: For shopping bags and general purpose films.
- Heavy-duty Bags: High tensile strength for heavy load bags.
- Food Packaging Bags: Good moisture barrier and food contact for food packaging.
- Industrial Bags: HDPE 7000F for industrial use bags.
- Disposal Waste Bags: Strong and durable waste disposal bags.
- Grocery Bags: A common and practical use is grocery bags.
- Garments: HDPE 7000F is also used in garment production, probably for packaging or components.
- Advanced Ultra-Thin Films: For films with minimal thickness and strength.
- Disposable Gloves: For thin film production of disposable gloves.
- Freezer Bags: Low-temperature resistance for freezer bags.
- Fruit Bags: Moisture barrier for fruit packaging.
- Trash Bags: Strong and durable for trash bags.
- Medical Gowns: HDPE 7000F is used in medical gown production, likely for disposable gowns.
- Value: Thin films mean material savings and cost reduction.
- Convenience: Easy to process and handle.
- Better Performance: High tensile strength, impact resistance, and moisture barrier properties to protect the contents.
- Versatility: Suitable for many applications.
- Packaging Industry: Bag, film, and pouch manufacturers for food, retail, and industrial applications.
- Food and Beverage: Companies looking for safe packaging solutions for their products.
- Medical: Gown and medical disposables.
- Retail: Bags for customer purchases.
Global oil prices fluctuate regularly, which affects the cost of products like hdpe 7000f. As a result, we do not have a fixed price for this item. To get the most current pricing information, please contact us directly. Should you have any questions regarding the prices, please contact us through WhatsApp for a prompt response.
- Standard Packaging: 25 kg PE-LD bags.
- Pallet Options: Stretch or shrink-wrapped pallets with a load of 1375 kg. Heat-treated pallets are also available.
- Bulk Packaging: Big bags with specified weight are available.
- Transportation: Road silo and rail silo transportation options are available.
| 0.04 | g/10min | ISO 1133 | Melt Flow Rate(2.16kg) |
| 952 | Kg/m3 | ISO 1183 | Density |
| – | Kg/cm2 | ASTM D 638 | Tensile Stress at Yield |
| 390 | Kg/cm2 | ASTM D 638 | Tensile Strength at Break |
| >500 | % | ASTM D 638 | Elongation at Break |
| 400 | hr | ASTM D 1693 | Stress Cracking Resistance (80°C) |
| 131 | °C | ASTM D 3418 | Melting Temperature |
| 30 | Kg.cm/cm | ASTM D 256 | Izod Notched (23°C) |
| Property | Unit | Condition | Typical Value | Test Method |
|---|---|---|---|---|
| Melt Flow Rate (MFR) | g/10min | 190°C/2.16 kg | 0.03-0.05 | ASTM 1238 |
| Density | g/cm³ | 23°C | 0.950-0.954 | ISO1183 |
| Melting Point | °C | – | 131 | ASTM D 2117 |
| Brittleness Temperature | °C | – | <-60 | ASTM D 746 |
| Dart Impact Strength | gr | – | 139 | ASTM D 1709 |
| Tensile Strength @ Yield | kg/cm² | MD | 250 | ASTM D 882 |
| Tensile Strength @ Yield | kg/cm² | TD | 620 | ASTM D 882 |
| Tensile Strength @ Break | kg/cm² | MD | 310 | ASTM D 882 |
| Tensile Strength @ Break | kg/cm² | TD | 8200 | ASTM D 882 |
| Tensile Modulus 2% Secant | kg/cm² | MD | 8000 | ASTM D 882 |
| Tensile Modulus 2% Secant | kg/cm² | TD | 240 | ASTM D 882 |
| Elongation @ Break | % | MD | 240 | ASTM D 882 |
| Elongation @ Break | % | TD | 450 | ASTM D 882 |
| Elmendorf Tear Str. | gr | MD | 80 | ASTM D 1922 |
| VICAT | °C | – | 124 | ASTM D 1525 |
| Property | Test Method | Value | Unit |
| Tensile Strength at Yield | ASTM D 638 @crosshead speed 50mm/min | MD: 380, TD: 250 | kg/cm² |
| Tensile Strength at Break | ASTM D 638 @crosshead speed 50mm/min | MD: 620, TD: 310 | kg/cm² |
| Tensile Modulus, 2% Secant | ASTM D 638 @ crosshead speed 50mm/min | MD: 8200, TD: 8000 | kg/cm² |
| Elongation at Break | ASTM D 638 @crosshead speed 50mm/min | MD: 240, TD: 450 | % |
| Elmendorf Tear Strength | ASTM D 1922 | MD: 3, TD: 80 | g |
| Dart Impact Strength | ASTM D 1709 | 139 | g |
| Gloss | ASTM D 2457 | 5.8 | GU |
| Haze | ASTM D1003 | 85.5 | % |