- GRADE: PE80
- DENSITY: 0.944 g/ml
- MFR: 0.33 g/10min
- PACKAGING: 25 kg Bags
- PRODUCER: ARYA SASOL
HDPE PE80
Description
HEX4460 PE80+ is a high molecular weight, high-density polyethylene with high melt viscosity for extrusion. This grade, which is produced by 1-hexene co-monomer, is classified as PE 80+ and provides excellent environmental stress crack resistance (ESCR) combined with very good long-term hydrostatic strength and good processability. HEX4460 PE80+ has been manufactured under a Basell license.
- Gas Distribution: HDPE PE80 is commonly used for gas pipes, particularly in residential and commercial settings, due to its ability to withstand pressure and resist corrosion.
- Water Supply: It is widely employed in potable water supply systems, ensuring safe and clean drinking water without leaching harmful substances into it.
- Industrial Applications: HDPE PE80 is suitable for transporting industrial fluids and chemicals, thanks to its high chemical resistance and strength.
- Sewage and Drainage Systems: The material is used in sewer systems and drainage applications, where its durability and resistance to environmental factors are crucial.
- Irrigation Systems: In agricultural settings, HDPE PE80 pipes are used for irrigation, providing reliable water delivery with minimal leakage.
- Processing Aid: No
- Antioxidant: Yes
- Antiblock: No
- Slip Agent: No
| Typical Properties | Typical Value | Unit | Test Method |
|---|---|---|---|
| Melt Flow Index (190oC/ 21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| Melt Flow Index (190oC/ 5.0 kg) | 0.33 | g/10 min | ISO 1133 |
| Density | 0.944 | g/cm3 | ISO 1183 |
| Tensile Strength at Yield | 25 | MPa | ISO 527-1, -2 |
| Elongation at Yield | 11 | % | ISO 527-1, -2 |
| Elongation at Break | >1000 | % | ISO 527-1, -2 |
| Tensile Strength at Break | 40 | MPa | ISO 527-1, -2 |
| Tensile Modulus of Elasticity | 700 | MPa | ISO 527-1, -2 |
| Flexural Modulus – 1% Secant | >1000 | MPa | ASTM D790 |
| ESCR F10 (10% Igepal, Method B) | >1000 | hrs | ASTM D1693 |
| FNCT (3.5 MPa, 2% Arkopal N100, 80oC) | >120 | hrs | ISO 16770 |
| Impact Tensile Impact Strength | 167 | kJ/m2 | ISO 8256 |
| Izod Impact Strength | 26 | kJ/m2 | ISO 180 |
| Melting Temperature | 129 | oC | ISO 3146 |
| Oxidation Induction Time | >30 | min | ISO 11357 |
| Vicat Softening Temperature | 126 | oC | ISO 306 |
| Deflection Temperature Under Load (0.45 MPa) | 68 | oC | ISO 75 |
| Deflection Temperature Under Load (1.8 MPa) | 50 | oC | ISO 75 |