- GRADE: HBM5510
- DENSITY: 0.955 gr/cm3
- MFR: 10 g/10 min
- HS Code: 39012000
- Packaging: 55*25 Kg shrink-wrapped wooden pallets
- PRODUCER: ARYA SASOL
HDPE HBM 5510
Описание
HBM 5510 is a high-density polyethylene (HDPE) specifically engineered for large parts blow molding applications. This versatile material is perfect for manufacturing jerrycans, open top drums, and intermediate bulk containers (IBCs). These products are essential for storing and transporting a wide range of liquids, including water, oil, chemicals, and food.
- Density: 0.955 g/cm³
- High Load Melt Flow Index (190°C/21.6 kg): 10 g/10 min
- Melt Flow Index (190°C/5 kg): 0.5 g/10 min
- Tensile Modulus of Elasticity: 1100 MPa
- Tensile Stress at Yield: 27 MPa
- Tensile Strain at Yield: 8%
- Tensile Impact Strength (Notched, -30°C): 135 kJ/m²
- Form: Pellet
- Additives: Contains antioxidant
- Jerrycans: Suitable for storing and transporting various liquids.
- Open Top Drums: Ideal for large-volume liquid storage.
- Intermediate Bulk Containers (IBCs): Perfect for bulk liquid transportation and storage.
- High stiffness and excellent mechanical properties.
- Good processability for efficient manufacturing.
- Excellent environmental stress crack resistance (ESCR) for durability.
| Property | Typical Value 1 | Unit | Test Method |
| High Load Melt Flow Index (190°C/21.6 kg) | 10 | g/10 min | ISO 1133 |
| Melt Flow Index (190°C/5 kg) | 0.50 | g/10 min | ISO 1133 |
| Density | 0.955 | g/cm³ | ISO 1183 |
| Bulk Density | >0.50 | g/cm³ | ISO 60 |
| Tensile Modulus of Elasticity | 1000 | MPa | ISO 527-1,2 |
| Flexural Modulus 1% Secant | 1000 | MPa | ASTM D790 |
| Tensile Stress at Yield | 27 | MPa | ISO 527-1,2 |
| Tensile Strain at Yield | 8 | % | ISO 527-1,2 |
| Tensile Stress at Break | 43 | MPa | ISO 527-1,2 |
| Ball Indentation Hardness | 49 | MPa | ISO 2039-1 |
| ESCR F50 (100% Igepal, Method B) | 110 | hrs | ASTM D1693 |
| Impact | |||
| Tensile Impact Strength (Notched, Type 1, Method A, -30°C) | 135 | kJ/m² | ISO 8256 |
| Izod Impact Strength (Notched, Method A, 23°C) | 22 | kJ/m² | ISO 180 |
| Thermal | |||
| Vicat Softening Temperature (Method A/ 10N) | 127 | °C | ISO 306 |
| Deflection Temperature Under Load (1.8 MPa) | 45 | °C | ISO 75 |
| Recommended Process Conditions | |||
| Extruder Barrel Temperature: 180-220 °C | |||
| Melt Temperature: 200-235 °C |